Alumina Mullite Corundum Refractory Bricks for High SiO2 Content and Optimal Strength

$Alumina Mullite Corundum Refractory Bricks for High SiO2 Content and Optimal Strength$

Alumina Mullite Corundum Refractory Bricks for High SiO2 Content and Optimal Strength

Categories	Special Firebrick
Place of Origin:	Henan, China
Model Number:	99,90
Brand Name:	Hong Tai
Packaging Details:	1.Pallet+Paper or Steel angle bead+Paper board +Plastic or Steel belt +Plastic film (1)Wooden pallet size:Usually0.920.92m(standard brick),but 11m (special shape brick) at most, (2)Load weight of each pallet:Usually 1.5-1.7Tons, max 2.0 Tons. (3
Supply Ability:	3000 Ton/Tons per Month high alumina refractory brick
MOQ:	2 tons
Price:	$1,500.00 - $2,000.00/tons
Shape:	Brick
Material:	Corundum
SiO2 Content (%):	0.15%--18.5%
Al2O3 Content (%):	80%-99.3%
MgO Content (%):	~
CaO Content (%):	~
Refractoriness (Degree):	1770°< Refractoriness< 2000°
CrO Content (%):	~
SiC Content (%):	~
Processing Service:	Bending, Welding, Punching, Decoiling, Cutting, Moulding
Product name:	corundum brick
Application:	Furnace Lining
Raw material:	Alumina
Color:	White
Apparent porosity/%:	16%~18%
Cold Crush Strength MPa:	>80
Bulk Density(g/cm3):	2.95-3.1
Size:	Customers' Requirement
Certificate:	ISO9001-2008
Brand:	Hong Tai

Contact Now

Add to Cart

Company Info.

Henan Hongtai Kiln Refractory Co.,Ltd.

View Contact Details

Product List

Haven't found right suppliers
Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
And this service is free of charge.
we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!

Submit Buying Request

Product Details
Company Profile

Alumina Mullite Corundum Refractory Bricks for High SiO2 Content and Optimal Strength

Product Description

Corundum refractory bricks are refractory products with alumina content greater than 90% and corundum as the main crystal phase. High normal temperature compressive strength (up to 340MPa). High load softening start temperature (greater than 1700 ° C). Very good chemical stability, strong resistance to acidic or alkaline slag, metals and glass liquids. Thermal shock stability is related to its organizational structure. Corundum bricks can be divided into sintered corundum brick and fused corundum brick.

Sintered alumina and fused corundum can be used as raw materials, or alumina clinker with high Al2O3 / SiO2 ratio can be combined with sintered alumina and made by sintering. It can also be made of non-burning corundum brick with phosphoric acid or other binders. Mainly used in iron-making blast furnace and blast furnace hot air furnace, steel-making furnace refining furnace, sliding water heater, glass melting furnace and petrochemical industry furnace.

As a professinal corundum refractory materials manufacturer, we have exported different corundum refractory bricks to more than 30 countires.Please kindly read the following and make Inquiry.

Specification

Items	Ultra Purity Corundum brick	99 Corundum brick	90 Corundum brick	Corundum Mullite Brick
Al2O3 %	≥99.3	≥ 98.5	≥ 90	≥80
SiO2 %	≤0.15	≤0.3	≤8.5	≤18.5
Fe2O3 %	≤0.1	≤0.2	≤0.2	≤0.3
Bulk density g/cm3	≥3.25	≥3.25	≥3.1	≥2.9
Apparent porosity %	≤18	≤18	≤18	≤18
Cold crushing strength MPa	≥100	≥100	≥100	≥100
Refractoriness under load (0.2Mpa,0.6%)	≥1700	≥1700	≥1700	≥1700
Reheating linear change rate (1600℃X 8h)	-0.2	-0.2	0.2	0.2
Thermal expansion % Tem.to 1300℃	8.1	8.1	8.1	7.6

Corundum brick white iron brick Features:

1.Alumina content is higher than 90%.

2.High compressive strength at room temperature (up to340MPa).

3.High load softening starting temperature (greater than 1700 ℃).

4.Good chemical stability, strong resistance to acidic or basic slag, metal and glass fluid, etc.

Corundum brick white iron brick Advantages :
1.high density& temperature resistibility
2. low bulk density, high compressive strength,
3. resistance to high temperature(≥1790℃)
4.good thermal shocking resistance
5.Excellent corrosion resistant to acids and alkalis
6. They are not influenced by H2, CO gases during use

Production progress

1.The corundum brick white iron brick Production Process
Crushing→Mixing→Shaping→Drying→Firing→Inspection→Packaging and Shipment

2.The corundum brick white iron brick Quality Assurance
HongTai Refractory is committed to high quality standards for all its products and services. With its thirst on State of the art technology at every level and a wide range of products, HongTai Refractory can provide ideal solutions for the stringent
requirement of the customer. Backed by decade of experience in different industries, and close association with customers,HongTai Refractory will always bring new products which will give better life and value to the user.

Packing & Delivery

China refractory manufacturer Corundum brick white iron brick for garbage incineration furnace, fluidized bed furnace

Straight size:230×114×65 230×114×75 230×57×65
Split size: 230×114×32 230×114×40 230×114×25 230×114×50
Arch/Wedge size: 230×114×65/45 230×114×65/55 230×114×75/45 230×114×75/55 230×114×75/65
Tile size: 230×230×38 230×230×50 230×230×65 230×230×75
Other size: Key brick, Skew brick, Soap, Checker, Neck, Taper
Also produce corundum bricks according to customers' needs

FAQ

Product Tags:


*From:	Your email address is incorrect!
*To:	Henan Hongtai Kiln Refractory Co.,Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!

Alumina Mullite Corundum Refractory Bricks for High SiO2 Content and Optimal Strength

Alumina Mullite Corundum Refractory Bricks for High SiO2 Content and Optimal Strength

Alumina Mullite Corundum Refractory Bricks for High SiO2 Content and Optimal Strength

silica refractory bricks

alumina silicate refractory brick

silica bricks refractory

Alumina Mullite Corundum Refractory Bricks for High SiO2 Content and Optimal Strength