| Categories | Transformer Core Material |
|---|---|
| Brand Name: | OHMALLOY |
| Model Number: | 1K107 |
| Certification: | ISO9001-2008 |
| Place of Origin: | China(Shanghai) |
| MOQ: | 50kg |
| Price: | negotiable |
| Payment Terms: | L/C, T/T, |
| Supply Ability: | 50000kg/month |
| Delivery Time: | 7 days |
| Packaging Details: | 100kg/wooden case |
| Material: | 1K107 |
| Thickness: | 0.025mm to 0.035mm |
| Shiled material: | Plastic, SS 304 |
| Package: | Wooden case |
| Width: | 30mm |
| Company Info. |
| Ohmalloy Material Co.,Ltd |
| Verified Supplier |
| View Contact Details |
| Product List |
Frequency Transformer Iron Core 50－60 Hz Long - Term Work Low Loss
Application area:Frequency transformer iron core(50－60Hz)
IF power transformer iron core (400Hz－15kHz)
Switch power transformer iron core ( below 10kHz)
Filter reactor, filtering and energy storage inductor,
Power factor correction inductor core( below 50kHz)
Saturable reactor,Pulse compressor iron core
High Saturation magnetic induction - reduce transformer volume
High magnetic permeability low coercive force- improve transformerefficiency
Low loss(Equivalent 1/3 1/5 of silicon steel sheet)- reduce transformer temperature rise
Good temperature stability - under 130℃ for long-term work
Typical Properties
Physical properties of FeSiB alloy
| Saturation magnetic induction (Bs) | 1.56T | Hardness (Hv) | 960 |
| Curie temperature (TC) | 410℃ | Density (d) | 7.18g/cm3 |
| Crystallizing temperature( Tx) | 550℃ | Resistivity(r) | 130mW-cm |
| Saturation magnetostriction coefficient (ls) | 27×10-6 | Continuous operating temperature range | -55－130℃ |
Magnetic properties of FeSiB alloy
| Product Type | Transverse magnetic annealing | No magnetic annealing | Longitudinal magnetic annealing |
| Maximum permeability | >2×104 | >20×104 | >25×104 |
| Saturation magnetic induction | 1.5 T | 1.5 T | 1.5 T |
| Residual magnetic induction | <0.5 T | 0.6-1.0 T | 1.2 T |
| Coercive force | <4A/m | <6 A/m | <2.5A/m |
| Loss(50Hz, 1.4T) | <0.2W/kg | <0.13W/kg | <0.25W/kg |
| Loss(400Hz, 1.2T) | <1.8W/kg | <1.25W/kg | <2W/kg |
| Loss(8kHz, 1.0T) | <80W/kg | <60W/kg | <100W/kg |
| Iron loss rate(-55°C –125C ) | <15% | <15% | <15% |
| Iron loss rate(120℃200 H) | <15% | <15% | <15% |
| Saturation magnetic induction(T) | 1.56 | 2.03 |
| Coercive force(A/m) | <4 | <30 |
| Maximum permeability(Gs/Os) | >25×104 | 4×104 |
| Iron loss(W/kg) | 50Hz, 1.3T <0.2 | 50Hz, 1.7T =1.2 |
| Exciting power (VA/kg) | 50Hz, 1.3T <0.5 | 50Hz, 1.7T <0.83 |
| Laminated coefficient | >0.80 | 0.95 |
| Magnetostriction(×10-6) | 27 | 15 |
| Resistivity(Wm-cm) | 130 | 45 |
| Density(g/cm3) | 7.18 | 7.65 |
| Tx(℃) | 550 | － |
| Curie temperature(℃) | 415 | 746 |
| Tensile strength(Mpa) | 1500 | 343 |
| Vickers hardness(HV) | 900 | 181 |
| Thickness(μm) | 30 | 300 |
(Size):
| grade | width (mm) | thickness (mm) |
| 1K107 | 3.2～50 | 27～36 |
Other specifications of the strip can be offered according to customer requirements.
|
Bright Annealed 1J50 Nickel Iron Magnetic Alloy For Power Transformers
High Frequency Nanocrystalline Strip For Transformer Iron Core Customized Size
Nanocrystalline Alloy 1K107 For Power Transformer And Pulse Transformer Iron Core
1K101 Transformer Iron Core Material Nanocrystalline Strip And Core 0.025mm Thickness
1K107 Transformer Core Material , Nanocrystalline Strip And Core 0.025mm Thickness
Ni79Mo4 Transformer Core Soft Magnetic Alloy E11c Ni 75-79% Chemical
1J50 Foil Transformer Iron Core High Magnetic Permeability 0.05mm Thick
0.027~0.03mm thickness,Large Power, High Frequency Transformer Iron Core, Good Temperature Stability
Leakage Protector Toroidal Transformer Core Material Fe Bal Chemical
Nanocrystalline Powe Transformer Core Material Plastic / SS 304 Shiled